Hand Lay-up and Spray-up

Polyester resins in this category are used in GRP hand lay-up, Spray-up, filament winding and continuous laminating applications. GRP type polyester resins are used in the production of many different products in many areas. Such as automotive parts, city furniture, modular cabins, bus, truck bodies, acrylic and acrylic-ABS bathtub production, yachts, boats, sea vehicles.
PRE-52AB PRE-52ABW PRE-52TAW PRE-52TADW PRE-52TADW(1) PRE-60 PRE-62 PRE-63 PRE-63A PRE-63TAB PRE-63TAB(LSE) PRE-521TADW PRE-631TAB(1) PRE-631TAB(2) PRE-631TAB(1)LSE PRE-6309TAB PRE-6309TAB(1) PRE-6309TAB(2)LSE PRE-6310TAB PRE-6311 PRE-6320 PRE-6324 PRE-6324 LV PRE-6324(1) PRE-6325 PRE-6325 LV PRE-6329
Description CTP Type (Acrylic Back Reinforcement) CTP Type CTP Type CTP Type (Acrylic Back Reinforcement) CTP Type (Acrylic Back Reinforcement) General Purpose General Purpose General Purpose General Purpose Thixotropic Thixotropic(Low Styrene Emission) CTP Type (Acrylic Back Reinforcement) Thixotropic Thixotropic Thixotropic Thixotropic Thixotropic Thixotropic Thixotropic General Purpose General Purpose General Purpose General Purpose General Purpose General Purpose General Purpose General Purpose
Chemical Content Orthophytalic / Standard Glycol Orthophytalic / Standard Glycol Orthophytalic / Standard Glycol Orthophytalic / Standard Glycol Orthophytalic / Standard Glycol Orthophytalic / Standard Glycol Orthophytalic / Standard Glycol Orthophytalic / Standard Glycol Orthophytalic / Standard Glycol Orthophytalic / Standard Glycol Orthophytalic / Standard Glycol Orthophytalic / Standard Glycol Orthophytalic / Standard Glycol Orthophytalic / Standard Glycol Orthophytalic / Standard Glycol Orthophytalic / Standard Glycol Orthophytalic / Standard Glycol Orthophytalic / Standard Glycol Orthophytalic / Standard Glycol Orthophytalic / Standard Glycol Orthophytalic / Standard Glycol Orthophytalic / Standard Glycol Orthophytalic / Standard Glycol Orthophytalic / Standard Glycol Orthophytalic / Standard Glycol Orthophytalic / Standard Glycol Orthophytalic / Standard Glycol
Properties in Liquid Form
Accelerator Yes Yes Yes Yes Yes Optional Optional Optional Yes Yes Yes Yes Yes Yes Yes Yes Yes Yes Yes Optional Optional Optional Optional Optional Optional Optional Optional
Reactivity Middle Middle Miscarriage Miscarriage Miscarriage High Middle Middle Middle Middle Middle Miscarriage Middle High Middle Middle Middle Middle Miscarriage Middle Middle Middle Middle Middle High High Middle
Thixotropy Optional Optional Yes Yes Yes Optional Optional Optional Optional Yes Yes Yes Yes Yes Yes Yes Yes Yes Yes Optional Optional Optional Optional Optional Optional Optional Optional
Viscosity (cPs) 200-250 200-250 180-200 180-200 180-200 180-200 300-450 340-460 340-460 900-1000 900-1000 2000-3000 1200-1400 250-350 1200-1400 300-400 300-400 300-400 450 - 550 1500-2500 350-550 450-550 450-550 450-550 550-650 300-400 700-800
Gel Duration (Min). 10-12 10-12 10-13 10-13 10-13 25-30 5-8 5-8 10-15 16-23 21-23 10-15 20-25 24-26 20-25 20-23 19-21 19-21 13-14 7 - 9 7-9 8-12 8-12 9-11 6-8 6-8 7-8
Monomer Rate % 32-38 32-38 32-38 32-38 32-38 33-37 34-38 34-38 34-38 35-45 40-45 25-35 30-35 35-45 30-35 30-40 30-40 30-40 40-45 35-40 31-37 31-37 35-40 35-40 30-35 31-35 30-35
Solid Properties
HDT °C 60-65 60-65 60-65 60-65 60-65 75-80 60-70 60-70 60-65 60-65 65-70 55-60 65-75 65-75 65-75 65-70 65-70 65-70 60-65 60-65 62-68 65-75 65-75 55-65 70-75 70-75 65-75
Barkol Hardness (934-1) 40-45 40-45 40-45 40-45 40-45 40-45 40 - 45 40-45 40-45 40-45 42-47 40-45 42-47 42-47 42-47 42-47 42-47 42-47 37-42 40-45 40-45 40-45 40-45 42-48 40-45 40-45 40-45
Trend Resistance (mPa) 100-120 100-120 100-120 100-120 100-120 110-130 110-130 110-130 100-120 100-120 110-130 60-70 110-130 110-130 110-130 110-130 110-130 110-130 105-125 115-125 125-135 120-130 120-130 110-130 140-150 140-150 125-145
Tensile Strength (mPa) 30-40 30-40 30-40 30-40 30-40 70-80 70-80 70-80 60-70 60-70 60-70 30-40 70-80 70-80 70-80 60-70 60-70 60-70 55-65 58-62 62-67 65-75 65-75 70-80 50-60 50-60 65-70
Impact Resistance (kj/m2) 5-10 5-10 5-10 5-10 5-10 10-15 5-15 5-15 6-10 6-10 8-12 5-8 5-15 5-15 5-15 8-12 8-12 8-12 8-12 7-10 7-10 6-10 6-10 6-8 8-12 8-12 7-10
Excellent adhesion to acrylic and ABS layer Excellent adhesion to acrylic and ABS layer Excellent adhesion to acrylic and ABS layer Excellent adhesion to acrylic and ABS layer Excellent adhesion to acrylic and ABS layer Rapid curing Good use features Good use features Good fiber wetting Low volumetric shrinkage Low volumetric shrinkage Excellent adhesion to acrylic and ABS layer Low volumetric shrinkage Low volumetric shrinkage Low volumetric shrinkage Low volumetric shrinkage Low volumetric shrinkage Low volumetric shrinkage Low volumetric shrinkage Low volumetric shrinkage Low volumetric shrinkage Without paraffin Without paraffin Without paraffin Low volumetric shrinkage Low volumetric shrinkage Quick curing
Excellent fiber wetting Excellent fiber wetting Excellent fiber wetting Excellent fiber wetting Excellent fiber wetting Low volumetric shrinkage Versatile use Versatile use Low volumetric shrinkage Bright and vibrant appearance Bright and vibrant appearance Excellent fiber wetting Excellent fiber wetting Without paraffin Contains paraffin Without paraffin Without paraffin Contains paraffin Bright and vibrant appearance High filler acceptance High filler acceptance Low volumetric shrinkage Low volumetric shrinkage Low volumetric shrinkage Good usage features Good usage features Rigid and High Mechanical Values
Features Due to its thixotropic feature, it does not flow on vertical surfaces. Due to its thixotropic feature, it does not flow on vertical surfaces. High filler acceptance High filler acceptance High filler acceptance Good use features Stable Gel Time Stable Gel Time Versatile use Quick and easy fiber wetting Quick and easy fiber wetting High filler acceptance It is thixotropic, does not flow on steep surfaces, Bright and vibrant appearance Bright and vibrant appearance Bright and vibrant appearance Bright and vibrant appearance Bright and vibrant appearance Quick and easy fiber wetting Good fiber wetting Good fiber wetting and easy rolling Quick and easy fiber wetting Quick and easy fiber wetting Quick and easy fiber wetting Contains paraffin Contains paraffin Low volumetric shrinkage
High filler acceptance High filler acceptance Contains Mek-P indicator Contains Mek-P indicator Contains Mek-P indicator High filler acceptance Good fiber wetting Low volumetric shrinkage Good handling properties and stable gel time Easy rolling Easy rolling Contains Mek-P indicator Without paraffin Easy rolling Easy rolling Easy rolling Easy rolling Easy rolling Easy rolling Easy application Fast demoulding Easy rolling Easy rolling Easy rolling Rapid curing Rapid curing High filler acceptance
Contains Mek-P indicator Contains Mek-P indicator Low volumetric shrinkage High filler acceptance High filler acceptance Contains Mek-P indicator Contains Mek-P indicator Contains Mek-P indicator Quick and easy fiber wetting Quick and easy fiber wetting Quick and easy fiber wetting Quick curing and easy fiber soaking Quick curing and easy fiber soaking Without paraffin Rigid and High Mechanical Values Low volumetric shrinkage Good marble powder wetting Good marble powder wetting
High filler acceptance Without paraffin Contains Paraffin Contains Mek-P indicator Contains Mek-P indicator Contains Mek-P indicator Contains Mek-P indicator Contains Mek-P indicator Contains Mek-P indicator
Technical Datasheet(TDS)
Saefty Datasheet(SDS)

Modification Codes

T Thixotropic LS Low Pick
A Cobalt Accelerator HV High Viscosity
B Blue Indiator LV Low Viscosity
D Filled UV UV Absorber
FR Flame Reterdant FT. Brush and Roll Application
LSE Low Strien Emissions TT Spray Application
ABP Amen Pre-Accelerator Colorful
WV Winter Version Transparent
SV Summer Version White Gelcoat
TE Teraftalic Acid W White Resin
FRHI Flame retardant Halogenated Isophthalide H Halogenated
FRH Flame Retardant Halogenated
Packing

You can choose the type of package you would like or contact our sales department for information about container options.